Firebrick
Anti Acid Brick |
||||||
Al2O3 (%) | 25% | |||||
SiO2 (%) | 70% | |||||
Fe2O3 | 1.5% | |||||
Refractoriness | -- | |||||
Bulk Density fm/c.c. | 2.0 - 2.1 | |||||
Cold Crushing Strength Kg/cm2 | > 700 | |||||
Service Temperature °C | 1280 | |||||
Porosity | 14 | |||||
Fire Clay Brick | SK 30 | SK 32 | SK 34 | |||
Al2O3 (%) | 30 | 34 | 42 | |||
SiO2 (%) | 65 | 52 | 54 | |||
Fe2O3 (%) | < 2.0 | < 2.0 | < 2.0 | |||
Bulk Density (gm/c.c) | 1.90 | 1.95 | 2.00 | |||
Porosity (%) | < 26 | < 26 | < 26 | |||
Cold Crushing Strength (Kg/cm2) | 200 | 230 | 250 | |||
Refractories (C) | 1450 | 1550 | 1650 | |||
Services Temperature (°C) | 1300 | 1300 | 1320 | |||
High Alumina Brick | SK 36 | SK38 | ||||
Al2O3 (%) | 55 | 70 | ||||
SiO2 (%) | 40 | 28 | ||||
Fe2O3 (%) | < 2.0 | 1.88 | ||||
Bulk Density (gm/c.c) | 2.10 | 2.913 | ||||
Porosity (%) | < 26 | < 26 | ||||
Cold Crushing Strength (Kg/cm2) | 300 | 476 | ||||
Refractories (°C) | 1790 | 1850 | ||||
Services Temperature (°C) | 1450 | 1500 | ||||
Plastic Materials | SK 34 | SK 36 |
|
|||
Al2O3 (%) | 42% | 55% | ||||
SiO2 (%) | 54% | 40% | ||||
Fe2O3 (%) | < 2% | < 2% | ||||
Method of Apply | Ramming or Casting | Ramming or Casting | ||||
Net Weight | 25kg/carton | 25kg/carton | ||||
Temperature (°C) | 1400°C | 1600°C |